316L stainless steel pipe-51 steel pipe network recommended:
1. The maximum carbon content of 316L stainless steel is 0.03, which can be used in applications where annealing cannot be performed after welding and maximum corrosion resistance is required.
316L stainless steel due to the addition of Mo, corrosion resistance, in particular, excellent resistance to pitting corrosion; high temperature strength is also very good; excellent work hardening (weak magnetic after processing); solid state without magnetic. 316L stainless steel number: 00Cr17Ni14Mo2
The experimental results showed that the chemical composition % C: ≤ 0.03 Si : ≤ 1.0 Mn : ≤ 2.0 Cr : 16.0 - 18.0 Ni : 12.0 - 15.0 S : ≤ 0.03 P : ≤ 0.045 Mo : 2.0 - 3.0.
2. 316 and 317 stainless steels (see below for properties of 317 stainless steel) are molybdenum-containing stainless steels.
3. The molybdenum content of 317 stainless steel is slightly higher than that of 316 stainless steel. Due to the molybdenum content in the steel, the overall performance of the steel is better than that of 310 and 304 stainless steels. Under high temperature conditions, when the sulfuric acid concentration is lower than 15% and higher than 85%, 316 stainless steel has a wide range of uses.
4. 316 stainless steel also has good chloride corrosion resistance, so it is usually used in the marine environment.
5. Corrosion resistance 6. Corrosion resistance is superior to 304 stainless steel and has good corrosion resistance in the production of pulp and paper.
7. And 316 stainless steel is also resistant to the erosion of the ocean and the aggressive industrial atmosphere. Heat resistance of 1600 degrees below the intermittent use and in 1700 degrees below continuous use, 316 stainless steel has good oxidation resistance.
8. In the range of 800-1575 degrees, it is better not to continuously apply 316 stainless steel, but when using 316 stainless steel continuously outside this temperature range, the stainless steel has good heat resistance.
9. 316L stainless steel has better carbide precipitation resistance than 316 stainless steel and can use the above temperature range.
10. Annealing is performed at a temperature in the range of 1850-2050 degrees, followed by rapid annealing, and then rapidly cooled.
11. 316 stainless steel can not be hardened by heat treatment.
12. Welding 13.316 stainless steel has good welding performance. All standard welding methods can be used for welding. Welding can be based on the use of 316Cb, 316L or 309Cb stainless steel filler rods or electrodes for welding. In order to obtain the best corrosion resistance, the welded section of 316 stainless steel needs post-weld annealing. If 316L stainless steel is used, post-weld annealing is not required.
14. Typical use of pulp and paper equipment, heat exchangers, dyeing equipment, film processing equipment, piping, and materials for coastal building exteriors Stainless steel seamless pipe production process a. Round steel preparation; b. Heating; c. Hot rolling piercing; d. Cut the head; e. Pickling; f. Grinding; g. Lubrication; h. Cold rolling processing; i. Degreasing; j. Solution heat treatment; k. Straightening; l. Cut tube; m. Pickling; n. Product testing.
316L stainless steel management theory weight formula: (OD - wall thickness) × wall thickness × 0.02513 = KG / M