Aluminum Strip Continuous Casting and Rolling Process Use

The aluminum strip casting and rolling process is an advanced production process imported from abroad in the 1980s. The basic flow is: aluminum ingotsâ†’smelting furnaceâ†’repose furnaceâ†’degassingâ†’filteringâ†’casting nozzleâ†’rolling millâ†’intermediary unitâ†’ Winder. Its characteristic is that the molten aluminum liquid is cast into a 6-10mm thick, 650-1400mm wide slab and rolled, and then directly sent to the cold rolling mill for finishing, so that in the production process of the aluminum strip, the ingot is omitted. Processes such as heating, hot rolling, and billet-opening not only shorten the process flow of aluminum sheet and strip production, but also greatly reduce the capital for engineering construction, and also reduce metal burn-in in the production process, save energy, and at the same time facilitate the realization of aluminum plates. Continuous production of strips. It is used to cold-roll aluminum and aluminum alloy coils, through the unit's uncoiling and cutting head, trimming, joint sewing, surface cleaning, drying, stretching, bending, straightening, board inspection, coiling and weaving process , Flattened, clean, uniform color, uniform shape of rolled product, suitable for the production of high-quality products requiring flat stone, no grease, surface water, paint coating, decoration and compounding. For hot rolling or Cold-rolled aluminum and aluminum alloy strips with horizontal shear or different length requirements of the plate off products, the machine line by the decoiling, feeding, cutting flattening, trimming waste edge processing, roll leveling, measuring shear, Equipment such as sampan plates, etc. Main product index materials, aluminum and aluminum alloys. Thickness: 0.3-12mm (designed according to different thicknesses) Width: 600-1560mm Cutting length: 500-4500mm Machine speed: 90m/min.